X-CERA HT: High strength and translucency, apply to coping, coping bridge, all kinds of bridges!
Our zirconia block is made of nanometer medical grade zirconia powder.
The powder is firstly compacted by cold isostatic pressing with high compressive strength and then pre-sintered to a certain degree to offer good machinability.
The zirconia blocks can be used to create crowns, bridges, inlays and veneers of fixed partial denture with different translucency levels and colors.
1. Open CAD CAM system like Roland, Wieland, Imes icore, VHF, Arum, Schutz, Yenadent, Sirona MCX5 and etc.
2. Zirkonzahn CAD CAM system.
3. Amann Girrbach CAD CAM sytem.
Chemical Composition
| Component | Content |
| ZrO2+HfO2 | ＞90.5wt% |
| Y2O3 | 9.28wt% |
| AL2O3 | ＜0.5wt% |
| Other Oxides | ＜0.5wt% |
Properties
| Projects | Detection result |
| Sintering Density | ≥6.0g/cm³ |
| Bending Strength | ≥750MPa |
| Vickers Hardness | 1250HV |
| Chemical Solubility | ＜100μg/m² |
Show case:
XTCEAR was founded in 2001,owning 20 years' R&D experience on Zirconium Dioxide Ceramic Material and Industrial CNC Milling Machine.
As a member of Aviation Industry of China(AVIC), XTCERA has 1400 employees and over 30,000 square meters R&D and production base.
FAQ:
Q1: Are you a manufacturer ?
Yes, we are one of the leader and professional manufacturer in China.
Q2: Are there differences among zirconia ceramics ?
Difference among zirconia ceramic can occur with the level of purity of zirconia, grain size, trace elements and stabilizing compounds, and consistency of formulation.
Difference can exist in shrinkage from batch to batch because of differences in the thermal expansion(CTE).